The physical properties of the catalysts

The appearance of gray white stripes or white ball

Specification - 3 ～ 5 × 5 ~ 10mm or 3 ~ 5mm in diameter

Push density: 0.7 ~ 0.85kg/1

Crushing strength: > 40N/

The product features and applications: LYT - 610 type dechlorination agent hashigh cleanliness, applicable to a wide range of characteristics, is an excellentdechlorination agent. It can make the raw material gas of chlorine in chlorine capacity below 0.1ppm, weight >14% (depending on process conditions). Chlorine gas is suitable for wide source, can be used to synthesis gas, hydrogen and nitrogen, carbon dioxide, carbon monoxide, chlorine gas hydrocarbon gases,especially suitable for low, protective agent of methanation catalyst. The general gas of chlorine in presence of hydrogen chloride to form, can use the method of chemical absorption, its removal.

Reflect principle

The reaction was: MO + HCL MCL+H2O

The normal application process conditions:

Operating pressure: 1 ~ 5Mpa

Operating temperature: room temperature to 400 ℃

Air speed: 1000 ~ 3000 H - 1

The height of the bed and column diameter ratio > 3

Import the HCL content in the feed gas < 200 ppm

To meet the above conditions are

The chlorine content of the export of raw materials: < 0.1 ppm

Dechlorination agent penetrating chlorine capacity: 14% (weight)

Dechlorination agent active component on chloride ion has strong adsorption capacity, the reaction can be completed in an instant, if the raw gas of chlorine in the form of organic chlorine, it should be the catalyst for hydrogenation conversioninto HCL hydrogenation, and LYT-610 removal.

Transportation and storage:

The 1 transport to avoid collision, falling roll, lest the dechlorination agent powderand packaging damage.

2 transport and storage to prevent damp.

3 should avoid contact with other chemicals, so as not to affect its activity.

4 as long as the seal intact, storage of 3 - 5 years, does not affect its activity, used as usual.

Matters needing attention:

1 for the inorganic form of chlorine removal in various materials, if the materialscontaining chlorine, you need to first hydrogenation conversion.

The 2 best reflected in the temperature range between 20 ~ 350 ° C.

Temporary parking of 3 systems, should maintain the chlorine reactor temperatureand pressure, in order to prevent the destruction of dechlorination performancecondensation medium inside the reactor, if necessary, can be dry gas exchange reactor, and holding pressure.

4 parking for dechlorination agent, should be under the sealed condition, coolingwith dry gas, and then discharge.